Cast Iron L-NiCr30-3

Designation

Name The value
Designation GOST Cyrillic L-NiCr30-3
Designation GOST Latin L-NiCr30-3
Transliteration L-NiCr30-3
The chemical elements L-NiCr30-3

Description

Cast iron L-NiCr30−3 is used: for the manufacture of casting parts for pumps, pressure vessels, valves, parts of filtering devices, exhaust piping and vessels turboiron devices.

Note

Nickel cast iron. Cast iron L-NiCr30−3 is resistant to heat and thermal shock to a temperature of 800 °C, good resistance to corrosion at high temperatures, high resistance to erosion in wet steam and salt slurry, the average degree of thermal expansion.

Standards

Name Code Standards
Castings with special properties (cast iron and steel) В83 GOST 7769-82

Chemical composition

Standard C Mn Cr Si Ni Fe Cu
GOST 7769-82 ≤2.5 0.5-1.5 2.5-3.5 1-2 28-32 The rest ≤0.5
Fe is the basis.

Mechanical characteristics

σB, MPa d4 Brinell hardness number, MPa
Castings on OST 1 90077-72
190-240 2-3 120-215

Description mechanical marks

Name Description
σB Limit short-term strength
d4 Elongation after rupture

Physical characteristics

Temperature Е, ГПа
20 98-113

A description of the physical symbols

Name Description
l Coefficient of thermal conductivity
a The coefficient of linear expansion