Steel 05Х15Н9Г6АМ (ЧС31)

Designation

Name The value
Designation GOST Cyrillic 05Х15Н9Г6АМ
Designation GOST Latin 05X15H9G6AM
Transliteration 05H15N9G6AM
The chemical elements 05Cr15Н9Mn6NMo
Name The value
Designation GOST Cyrillic ЧС31
Designation GOST Latin ChC31
Transliteration ChS31
The chemical elements ZrС31

Description

05Х15Н9Г6АМ steel is used: for the production of forged blanks intended for the manufacture of welding wire.

Standards

Name Code Standards
Bulls. Blanks. Slabs В31 TU 14-1-1588-76

Chemical composition

Standard C S P Mn Cr Si Ni Fe N Mo
TU 14-1-1588-76 ≤0.05 ≤0.02 ≤0.02 5.5-7 14.5-15.5 ≤0.4 9-10 The rest 0.12-0.22 1.4-1.8
Fe is the basis.
According to TU 14-1-1588-76 the chemical composition is presented for steel grade Sv-05H15N9G6AM. Deviations in chemical composition are permissible: in manganese + 0.50%, in silicon +0.050%, in chromium ± 0.25%, in nickel ± 0.25%, in molybdenum ± 0.20%. Other deviations are allowed by agreement of the parties.

Mechanical characteristics

Section, mm sT|s0,2, MPa σB, MPa d5, % y, % kJ/m2, кДж/м2
Ingots on the other 14-1-1588-76. Annealing in air 1050°C (in the graph indicated KCU KCU+20°C/KCU-196°C)
≥245 ≥590 ≥40 ≥50 ≥1960/980

Description mechanical marks

Name Description
Section Section
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture
y The relative narrowing
kJ/m2 Toughness

Technological properties

Name The value
Macrostructure and contamination The macrostructure of the steel on the other 14-1-1588-76, check on cross microtemplate taken from the supplied profile should not have shrinkage porosity, gas bubbles, cracks, inclusions, electraprobe, inversion of the crust and other defects visible to the naked eye. Permitted defects of a macrostructure: Central porosity - 1 point, point heterogeneity - 1 point; - exudation square - 1 point. On the open metal smelting allowed the increase of the score of defects allowed to 2. In the metal ESR allowed layer-by-layer crystallization and light the path to a score of 3.
Features of production Supply on the other shall be 14-1-1588-76 the metal is melted in the open arc electric furnaces, plasma arc furnaces, and also obtained by the method of electroslag remelting.