Steel 07Х12НМФБ (ЧС80)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
07Х12НМФБ |
| Designation GOST Latin |
07X12HMFB |
| Transliteration |
07H12NMFB |
| The chemical elements |
07Cr12НMoVNb |
| Name |
The value |
| Designation GOST Cyrillic |
ЧС80 |
| Designation GOST Latin |
ChC80 |
| Transliteration |
ChS80 |
| The chemical elements |
ZrС80 |
Description
07Х12НМФБ steel is used: for the production of forged billets with a diameter of 90−180 mm, used for the manufacture of tubes and tube plates of steam generators and nuclear power plant equipment and power plants, operating in conditions of superheated steam at temperatures up to 550−600 °C.
Note
Steel corrosion resistant low carbon martensitic class.
Standards
| Name |
Code |
Standards |
| Bulls. Blanks. Slabs |
В31 |
TU 14-1-4092-86 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
N |
Al |
V |
Mo |
Nb |
| TU 14-1-4092-86 |
0.05-0.08 |
≤0.02 |
≤0.02 |
0.3-0.8 |
11.5-13 |
≤0.2 |
0.8-1.3 |
The rest |
≤0.035 |
≤0.15 |
0.05-0.2 |
0.8-1 |
0.05-0.2 |
Fe is the basis.
According to TU 14-1-4092-86, the chemical composition is given for steel grade 07Х12НМФБ (ЧС-80), smelted in a plasma or electric arc furnace. Limit deviations from the chemical composition in the workpiece: carbon +0.010%, chromium-0.50%, nitrogen +0.010%, molybdenum ± 0.050%, silicon +0.10%. The residual content of the elements must comply with GOST 5632. Other deviations from the chemical composition of the steel are agreed with the consumer enterprise. At the customer's request, the steel can be doped with boron no more than 0.0050% by calculation without determining by chemical analysis.
Mechanical characteristics
| Section, mm |
sT|s0,2, MPa |
σB, MPa |
d5, % |
y, % |
kJ/m2, кДж/м2 |
| Tubular billet forged on the other 14-1-4092-86. Normalization at 1050±20 °C, air cooling + Vacation at 740±20 °C, air cooling (longitudinal samples) |
| 20-25 |
≥490 |
≥638 |
≥15 |
≥60 |
≥1180 |
| 20-25 |
≥343 |
≥440 |
≥12 |
≥55 |
- |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σB |
Limit short-term strength |
| d5 |
Elongation after rupture |
| y |
The relative narrowing |
| kJ/m2 |
Toughness |
Technological properties
| Name |
The value |
| Pressure treatment |
The degree okowa a tube blank on the other 14-1-4092-86 must be at least 3 for a diameter over 120 mm and at least 5 for diameter to 120 mm, inclusive. |
| Macrostructure and contamination |
The macrostructure of billets on the other 14-1-4092-86 should not be visible without using the magnifying devices podnasadochnogo looseness, cracks, foreign non-metallic inclusions, subcortical bubbles and delamination. The defects allowed must not exceed: - for a point heterogeneity - 2 points; - for Central porosity - 2 points; - phase separation in the square - 2 points; - podsadecki segregation - 1 grade. Contamination of billets non-metallic inclusions in the evaluation by the maximum score shall not exceed: - sulphides (C) - 3.0 points; -oxides of stroke (OS) - 4.0 points; - point oxides (FROM) - 3.0 points; - silicates fragile (CX) - 3.0 points; - silicates plastic (SP) - 3.0 points; - silicates, non-deformed (CH) - 3.0 points; - nitrides and carbonitrides stroke (NA) - 3.0 points; - nitrides and carbonitrides point (NT) and 3.0. |
| Corrosion resistance |
Increased resistance to pitting corrosion. |