Steel 10KH14AG15 (DI-13)

Steel 10Х18Н5Г9АС4 (EP492; VNS-3) Steel 10Х32Н4Д (EP529) Steel 10Х17Н5М2 (EP405) Steel 10Х17Н13М3Т (ЭИ432) Steel 10Х17Н13М2Т (ЭИ448) Steel 10Х14Г14Н3 (DI-6) Steel 10Х14АГ15 (DI-13) Steel 09Cr17N7Yu1 (0Cr17N7Yu1) Steel 09Х17Н7Ю (ЭИ973) Steel 09Х16Н4Б (EP56; 1Х16Н4Б) Steel 09Х15Н8Ю1 (09Х15Н8Ю; ЭИ904) Steel 08ХГСДП Steel 08Х22Н6Т (EP53) Steel 08Х21Г11А6 (VNS-53) Steel 08Х20Н4АГ10 (НН-3) Steel 08X18Th (DI-77) Steel 08Х18Н7Г10АМ3 (08Х18Н7Г10АМ3С2) Steel 08Cr18Ni5G12AB (HH-3B) Steel 08X18H5G11BAF (HH-3BF) Steel 08X18H4G11AF (HH-3F) Steel 08Cr18Ni12T (0Cr18Ni12T) Steel 08X18H12B (EI402) Steel 08Х18Г8Н2Т (KO-3) Steel 08Cr17Ni6T (DI-21) Steel 20Х13Н4Г9 (ЭИ100) Cr17N14M3T steel Cr17N14M2T steel Steel 95X18 (EI229) Steel 95X13M3K3B2F (EP766) Steel 65X13 Steel 40X13 (4X13) Steel 30X13 (3X13) Steel 26Х14Н2 (EP208) Steel 25X17H2B Steel 25X17H2 (EP407) Steel 25Х13Н2 (ЭИ474) Steel 20X17H2 (2X17H2) Steel 08Х17Н15М3Т (ЭИ580) 18X13H3 steel Steel 15Х18Н12С4ТЮ (ЭИ654; 2Х18Н12С4ТЮ) Steel 15Х17АГ14 (ЭП213) Steel 13Х18Н10Г3С2М2 (ЗИ98) Steel 12Х21Н5Т (ЭИ811; 1Х21Н5Т) Steel 12Х18Н13АМ3 (EP878) Steel 12X18H10E (EP47) Steel 12Х17Н8Г2С2МФ (ЗИ126) Steel 12X17G9AN4 (EI878) Steel 12Х13Г12АС2Н2 (DI50) Steel 11Х13Н3 Steel 03Х16Н15М3 (ЭИ844) 04X15ST steel Steel 04X17H10M2 Steel 03Х23Н6 (ЗИ68) Steel 03Х22Н6М2 (ЗИ67) Steel 03Х21Н25М5ДБ Steel 03Х21Н21М4ГБ (ЗИ35) Steel 03Х20Н45М5Б (ChS32; 03ХН45МБ) Steel 03Х18Н12Т (000Х18Н12Т) Steel 03Х18Н12 (000Х18Н12) Steel 03X18N11 (000X18N11) Steel 03Х17Н14М2 Steel 03X17AN9 (EK177) 04X17T steel Steel 03Х15Н35Г7М6Б (EP855) Steel 03X13AG19 (ChS36) Steel 03Х12Н10МТР (EP810; VNS-25) Steel 03Х12К10М6Н4Т (EP927) Steel 03Х11Н10М2Т2 (EP853) Steel 02Х25Н22АМ2 (ChS108) Steel 02Х21Н25М5ДБ (EC5) Steel 02Х21Н21М4Г2Б (ЗИ69) 02Cr18Ni11 steel Steel 02X17H14M3 Steel 015Х16Н15М3 Steel 06Х14Н6Д2МБТ (EP817) Steel 08Х17Н13М2Т (0Х17Н13М2Т; ЭИ448) Steel 08Х10Н20Т2 (0Х10Н20Т2) Steel 08Х10Н16Т2 (0Х10Н16Т2) Steel 07X21G7AN5 (EP222) Steel 07X18N10P (EP287) Steel 07Х16Н6 (EP288; СН-2А; Х16Н6) Steel 07Х16Н4Б Steel 07Х15Н7М2 (EP35; СН-4; Х15Н8М2Ю) Steel 07Х16Н6 Steel 06X18H11 (EI684) 06X15H4DM steel Steel 08Х17Н5М3 (ЭИ925) 06X13H4DM steel Steel 06Х12Н3Д Steel 06Х12Н3Д (08Х12Н3Д) 05KhGB steel Steel 05Х20Н15АГ6 (ChS109) Steel 05Х12Н9М2С3 (EP821) Steel 05Х12Н2К3М2АФ (VNS-40) Steel 04Х32Н8 (EP535) Steel 04Х25Н5М2 (DI62) Steel 04X19MAFT Steel 04X18H10 (EI842)

Designation

Name The value
Designation GOST Cyrillic 10Х14АГ15
Designation GOST Latin 10X14AG15
Transliteration 10H14AG15
The chemical elements 10Cr14NMn15
Name The value
Designation GOST Cyrillic ДИ-13
Designation GOST Latin DI-13
Transliteration DI-13
The chemical elements CuИ-13

Description

10KH14AG15 steel is used: for the manufacture of non magnetic parts that work in slightly aggressive environments; household articles and parts of washing machines; the various parts and structures, welded by spot welding; the various parts of aviation.

Note

Steel corrosion resistant austenitic class.
Substitute cold-rolled steel grades 12H18N9 and 17H18N9 for strong and light structures connected by spot welding.

Standards

Name Code Standards
Sheets and stripes В33 GOST 5582-75, TU 14-1-1309-75
Classification, nomenclature and general norms В30 GOST 5632-72
Bulls. Blanks. Slabs В31 OST 3-1686-90
Sectional and shaped rolling В32 TU 14-11-245-88

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu N Ti Mo
GOST 5632-72 ≤0.1 ≤0.03 ≤0.045 14.5-16.5 13-15 ≤0.8 ≤2 The rest ≤0.6 0.15-0.25 ≤0.2 ≤0.3
Fe is the basis.

Mechanical characteristics

sT|s0,2, MPa σB, MPa d5, % y, %
Rolled steel. Quenching in water from 1050 °C
≥96 ≥205 ≥44 ≥46
Sheet-section 3 mm. Quenching in water from 1050 °C (indicated by the degree of deformation in %)
370-420 700-860 ≥60 -
Hot rolled sheet (of 1.5-3.9 mm) and cold rolled (0,7-3,9 mm) steel according to GOST 5582-75. Quenching in water with 950-1110 °C
- ≥740 ≥45 -
Rolled steel. Quenching in water from 1050 °C
≥75 ≥125 ≥57 ≥57
Sheet-section 3 mm. Quenching in water from 1050 °C (indicated by the degree of deformation in %)
920-960 1040-1140 ≥32 -
Rolled steel. Quenching in water from 1050 °C
≥43 ≥61 ≥64 ≥56
Sheet-section 3 mm. Quenching in water from 1050 °C (indicated by the degree of deformation in %)
1080-1210 1080-1210 ≥18 -
Rolled steel. Quenching in water from 1050 °C
≥33 ≥44 ≥82 ≥61
Sheet-section 3 mm. Quenching in water from 1050 °C (indicated by the degree of deformation in %)
1410-1560 1520-1680 ≥7 -
Rolled steel. Quenching in water from 1050 °C
≥20 ≥29 ≥64 ≥58
≥10 ≥20 ≥64 ≥59

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture
y The relative narrowing

Physical characteristics

Temperature Е, ГПа r, кг/м3 a, 10-6 1/°С
0 205 7900 -
20 205 7900 -
400 179 - 194
100 - - 139
300 - - 139
600 - - 194
800 - - 218
1000 - - 225

A description of the physical symbols

Name Description
r Density
l Coefficient of thermal conductivity
R UD. the resistivity

Technological properties

Name The value
Weldability without restrictions. It is recommended that RDS standard electrodes. Well welded in shielding gas without the additive and with the additive wire, the basic structure or composition of the type Х18Н9. Not allowed contact welding with low alloy or carbon steel due to the formation of brittle structures in the core of the point. Additional treatment of welded joints is not required.
Forging temperature Start - 1160 °C, the end - 850 °C.