Steel 13Х15Н4АМ3 (ЭП310; ANS-5)

Steel 1Х14Н14В2М (ЭИ257) Steel 13Х15Н4АМ3 (EP310; VNS-5) Steel 15X11MF (1X11MF) Steel 15Х12ВНМФ (ЭИ802) Steel 15Х12Н2МВФАБ (EP517) Steel 15Х16К5Н2МВФАБ (EP866; VNS-30) Steel 16Х11Н2В2МФ (ЭИ962А) Steel 16Х12ВМСФ5Р Steel 16X12MVSFBR (EP823) 18X11MNFB steel (EP291) Steel 18Х12ВМБФР (ЭИ993) Steel 18Х14Н4АМ3 (VNS-43) 18Kh15N3M steel (DI1) Steel 13Х11Н2В2МФ (ЭИ961; ВНС-33) Steel 20X12VNMF (EP428; 20X12VNMF-S (EP427-S)) Steel 25Х13Н2ВМФ (EP65; 2Х13НВМФ) Steel 25Х18Н10В2 (EP610) Steel 25Х18Н8В2 (ЭИ946) Steel 31Х19Н9МВБТ (ЭИ572) Steel 37Х12Н8Г8МФБ (ЭИ481) Steel 40Х15Н7Г7Ф2МС (ЭИ388) Steel 42Х11М3Ф (EP890) Steel 45Х14Н14В2М (ЭИ69) Steel 45Х14Н14СВ2М (ЭИ240) Steel X12H20T2P (EI696A) X14H8M2 steel (EP509) Cr18N13C2AMVF5P steel Steel 09Х14Н19В2БР1 (ЭИ726) Steel 01X19Yu3Bch (EP904; 02X18Yu3B) Steel 04Х15Н11С3МТ Steel 06X14H5MF Steel 06Х16Н15М3Б (ЭИ847; 06Х16Н15М3Б) 06X16H15M3K steel Steel 07Х25Н16АГЦ (EP781) Steel 08X14MF Steel 08Х15Н24В4ТР (EP164) Steel 08Х15Н25М3ТЮБ Steel 08Х15Н5Д2Т (EP410; VNS-2; EP225) Steel 08Х16Н13М2Б (ЭИ680) Steel 09X14H16B (EI694) Steel 09X14H19V2BR (EI695R) Steel 13Х14Н3В2ФР (ЭИ736; 513Л) Steel 09Х16Н13М3 (ЭИ592) Steel 09Х16Н15М3Б Steel 09Х16Н16МВ2БР (ЭП184; Х16Н16МВ2БР) Steel 09Х16Н7М2Ю (ЗИ65) 10GN2MFA steel Steel 10Х11Н20Т3Р (ЭИ696) Steel 10Х11Н23Т3МР (ЭП33; ЭЦ696) Steel 10Х12Н22Т3МРУ (EP33U) Steel 10Х15Н28В2М4Б (EP485) Steel 10Х15Н9С3Б1 (EP302) 10Х9НСМФБ steel Steel 11Х11Н2В2МФ (ЭИ962)

Designation

Name The value
Designation GOST Cyrillic 13Х15Н4АМ3
Designation GOST Latin 13X15H4AM3
Transliteration 13H15N4AM3
The chemical elements 13Cr15Н4NMo3
Name The value
Designation GOST Cyrillic ЭП310
Designation GOST Latin EP310
Transliteration EhP310
The chemical elements -
Name The value
Designation GOST Cyrillic ВНС-5
Designation GOST Latin BHC-5
Transliteration VNS-5
The chemical elements WНС-5

Description

13Х15Н4АМ3 steel is used: for the manufacture of forgings intended for subsequent cold machining or hot for subsequent machining (stamping, forging, rolling, etc.) in the manufacture of machine parts; special heat-resistant fasteners for power equipment.

Note

Corrosion-resistant steel austenitic-martensitic class.

Standards

Name Code Standards
Classification, nomenclature and general norms В20 OST 1 90005-91
Bulls. Blanks. Slabs В21 OST 1 90176-75
Bulls. Blanks. Slabs В31 TU 14-1-1213-75, TU 14-1-1214-75, TU 14-1-1626-76
Sheets and stripes В33 TU 14-1-1505-76, TU 14-1-2931-80
Metal forming. Forgings В03 TU 14-1-1530-75, TU 14-1-2902-80, TU 14-1-2918-80
Sectional and shaped rolling В32 TU 14-1-940-74, TU 14-1-1271-75

Chemical composition

Standard C S P Mn Cr Si Ni Fe N B Mo
TU 14-1-2902-80 0.11-0.16 ≤0.02 ≤0.03 ≤1 14-15.5 ≤0.7 4-5 The rest 0.05-0.11 0.11-0.16 2.3-2.8
TU 14-1-1505-76 0.11-0.16 ≤0.02 ≤0.03 ≤1 14-15.5 ≤0.7 4-5 The rest 0.05-0.1 - 2.3-2.8
Fe is the basis.
According to TU 14-1-2902-80, TU 14-1-2918-80 and TU 14-1-1505-76 the chemical composition is given for 13Х15Н4АМ3-Ш (ЭП310-Ш).
According to TU 14-1-1505-76 deviations from the norms of chemical composition are allowed: for carbon -0.010%, for chromium, nickel and molybdenum ± 0.10% of each element.

Mechanical characteristics

Section, mm t отпуска, °C sT|s0,2, MPa σB, MPa d5, % y, % kJ/m2, кДж/м2 Brinell hardness number, MPa HRC
Gradation of performance properties of the finished heat-treated parts for OST 1 90005-91
- - - 1350-1570 - - - - 39.5-45.5
- - - 1470-1670 - - - 415-462 43-46
Forgings. Quenching in air, water or oil 1060-1080 °C + cold Treatment at minus 70°C (2 h) or -50 °C (4 hours) + Holiday
450, 1 ч ≥1030 ≥1420 ≥15 ≥55 ≥980 - -
190-210, 2 ч ≥1080 ≥1470 ≥15 ≥50 ≥980 - -
Sheet rental on the other 14-1-1505-76. The normalization in the air with 1060-1080 °C + cold Treatment at minus 70±5 °C (2 h ± 10 min) + Aging at 450±10 °C (1 h ± 10 min.)
- ≥1030 ≥1422 ≥10 - - - -
Forming at OST 1 90176-75. Quenching in air, water or oil 1060-1080 °C + cold Treatment at minus 70°C (2 h) or -50 °C (4 hours) + Holiday
450, 1 ч ≥1030 ≥1422 ≥15 ≥55 ≥980 - -
190-210, 2 ч ≥1079 ≥1472 ≥15 ≥50 ≥980 - -

Description mechanical marks

Name Description
Section Section
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture
y The relative narrowing
kJ/m2 Toughness
HRC Rockwell hardness (indenter diamond spheroconical)