Alloy 1915

Alloy 01311C Alloy 1105 Alloy 1151 Alloy 1161 Alloy 1163 Alloy 1201 Alloy 1205 Alloy 1213 Alloy 1215 Alloy 1320 Alloy 1370 Alloy 1420 (01420) Alloy 1424 Alloy 1430 Alloy 1440 Alloy 1441 Alloy 1450 Alloy 1531 Alloy 1541 Alloy 1541pc Alloy 1543 Alloy 1577 Alloy 1905 Alloy 1911 Alloy 1915 Alloy 1925 Alloy 1931 Alloy 1933 Alloy 1935 Alloy 1953 Alloy 1955 Alloy 1973 Alloy 1980 (B48-4) Alloy 1985h Alloy 8011 Alloy 8011A Alloy 8111 Alloy A1Mg1M1 Alloy ABT101 (1901) Alloy ABT102 (1903) Alloy AB (1340) Alloy AVD1 Alloy AVD1-1 ABE Alloy Alloy AD1pl Alloy AD31 (1310) Alloy AD31E (1310E) Alloy AD33 (1330) Alloy AD35 (1350) Alloy AW Alloy AZh0.6 Alloy AZh0.8 Alloy AZh1 Alloy AK10 (SvAK10) AK12D alloy Alloy AK4 (1140) Alloy AK4-1 (1141) Alloy AK4-2 (1143) Alloy AK5 Alloy AK6 (1360) Alloy AK6-1 Alloy AK8 (1380) AKM Alloy Alloy AKCM Alloy AM4 Alloy AMg0.5 (1505) Alloy AMg0,5pc Alloy AMg0.7 Alloy AMG1 (1510) Alloy AMg1.5 Alloy AMg2 (1520) Alloy AMg2.5 Alloy AMg3 (1530) Alloy AMg3.5 Alloy AMg3S Alloy AMg4 (1540) Alloy AMg4.5 Alloy AMg5 (1550) Alloy AMg5P (1557) Alloy AMg6 (1560) Alloy AMg61 (1561) Alloy AMg61H (1561H) Alloy AMg63 (СвАМг63) Alloy AMg65 Alloy AMSH1 Alloy AMSH2 Alloy AMZ (1400) Alloy AMTS (1401) Alloy AMSh1 (AMSh-1) Alloy APBA-1 (1551) Alloy ACpl Alloy B-1341 Alloy B-1461 Alloy B-1469 Alloy B-1963 Alloy B48P Alloy B65 (1165) Alloy B91 (1913) Alloy B92 (1920) Alloy B93 (B93pch; 1930) Alloy B94 (1940) Alloy B95 (1950) Alloy B95-1 Alloy B95-2 Alloy B95och Alloy B95P (1957) Alloy B95pch Alloy B96C (1960) Alloy B96C1 Alloy B96C3 (1965-1) Alloy VD1 Alloy VD17 (1170) Alloy D1 (1110) Alloy D12 (1521) Alloy D16 (1160) Alloy D16P (1167) Alloy D18 (1180) Alloy D19 (1190) Alloy D19P (1197) Alloy D19h Alloy D1P (1117) Alloy D20 (1200) Alloy D21 (1210) Alloy D23 (WAD23; 1230) Alloy D24 (VAD1; 1191) Alloy K48-1 Alloy K48-2 (1941) Alloy K48-2pch (1943) Alloy K48P Alloy M40 Alloy MM (1403) Alloy SAB1 Alloy SAW2 Alloy SAB6 Alloy SAB9 Alloy SIL 1C Alloy SIL 2S

Designation

Name The value
Designation GOST Cyrillic 1915
Designation GOST Latin 1915
Transliteration 1915
The chemical elements 1915

Description

Alloy 1915 used: for the manufacture of pipes and fittings special branches of engineering; the manufacture of various nesvorny in construction, mechanical engineering and aircraft construction; large extruded tubes; extruded by hot extrusion of profiles of constant cross section for use in enclosing building constructions and products.

Note

The alloy system Al-Zn-Mg.
ISO 209−1 alloy brand designation in 1915 has AlZn4,5Mg1,5Mn and 7005.

Standards

Name Code Standards
Tapes В54 GOST 13726-97, OST 1-92006-79
Sheets and stripes В53 GOST 17232-99, GOST 21631-76, OST 4-021.049-78, OST 4.021.047-92, TU 1-2-390-79, TU 1-2-84-85, TU 1-804-473-2009
Pipes from non-ferrous metals and alloys В64 GOST 18482-79, OST 1 92048-90, OST 1 92048-76, OST 4.021.121-92, TU 1-2-162-79, TU 1-2-393-79, TU 1-5-211-83, TU 1-83-26-75, TU 1-9-483-77, TU 1-9-506-74
Bars В55 GOST 21488-97, OST 1 92019-72, TU 1-2-253-78
Non-ferrous metals, including rare metals, and their alloys В51 GOST 4784-97, OST 1 92014-90, OST 4.021.009-92
Sectional and shaped rolling В52 GOST 8617-81, GOST 13616-97, GOST 13617-97, GOST 13618-97, GOST 13619-97, GOST 13620-90, GOST 13621-90, GOST 13622-91, GOST 13623-90, GOST 13624-90, GOST 13737-90, GOST 13738-91, GOST 17575-90, GOST 17576-97, GOST 29296-92, GOST 29303-92, GOST Р 50066-92, GOST Р 50067-92, GOST Р 50077-92, GOST 22233-93, GOST 22233-83, OST 1 92093-83, OST 1 92022-73, OST 4.021.133-92

Chemical composition

Standard Mn Cr Si Fe Cu Al Ti Zn Zr Mg
TU 1-804-473-2009 0.2-0.7 0.06-0.2 ≤0.35 ≤0.4 ≤0.1 The rest 0.01-0.06 4-5 0.08-0.2 1-1.8
Al is the base.
According to GOST 4784-97, the mass fraction of each other impurity (not regulated) is ≤ 0.05%, the total mass fraction of other impurities is ≤ 0.15%.

Mechanical characteristics

Section, mm sT|s0,2, MPa σB, MPa d
The tape is able to supply for OST 1-92006-79
1-10.5 ≥164.6 ≥264.6 ≥10
1-4.5 - ≤245 ≥10
1-10.5 ≥196 ≥313.6 ≥10
Sheet metal in delivery condition according to GOST 21631-76, OST 4.021.047-92 tape according to GOST 13726-97 (samples transverse)
5-10 315-265 - ≥10
1-4.5 - ≤245 ≥10
1-10.5 ≥165 ≥275 ≥10
1-10.5 ≥195 ≥315 ≥10
Plate in the delivery condition on the other 1-804-473-2009
11-20 ≥195 ≥315 ≥10
11-20 ≥165 ≥275 ≥10
Plates according to GOST 17232-99 in the delivery condition (transverse specimens)
11-20 ≥195 ≥315 ≥10
11-20 ≥165 ≥275 ≥10
Extruded normal strength according to GOST 8617-81 in the delivery condition (longitudinal samples)
12 ≥167 ≥265 ≥10
12 ≥196 ≥314 ≥10
≥176 ≤277 ≥12
150 ≥176 ≥275 ≥10
150 ≥216 ≥343 ≥10
12-150 ≥245 ≥373 ≥8
The extruded profiles according to GOST 22233-93 in the delivery condition. Without heat treatment with natural aging 30-35 days
12 ≥196 ≥314 ≥10
The pressed bars normal strength in the delivery condition according to GOST 21488-97 (longitudinal samples)
8-300 - ≥275 ≥12
8-15 ≥165 ≥275 ≥10
8-15 ≥195 ≥345 ≥10
130-200 ≥245 ≥355 ≥8
8-130 ≥245 ≥375 ≥8
Tubes extruded in the state of delivery according to GOST 18482-79 (samples, in cross-section shows the thickness of the wall)
≥155 ≥265 ≥10
≥195 ≥315 ≥10
≥165 ≥275 ≥10
≥215 ≥355 ≥10
Large-size extruded tubes according to OST 1 92048-76 on delivery
≥196 ≥314 ≥10
≥216 ≥353 ≥10

Description mechanical marks

Name Description
Section Section
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d Elongation after rupture

Physical characteristics

Temperature r, кг/м3
20 2770

A description of the physical symbols

Name Description
Е The normal elasticity modulus
r Density
l Coefficient of thermal conductivity
С Specific heat

Technological properties

Name The value
Weldability Well welded alloy system Al-Zn-Mg and under certain conditions can be successfully used in the construction instead of welding AMg6 alloy, which is inferior to the alloy of 1915 on the strength characteristics, especially yield stress.
Pressure treatment 1915 alloy well deformed in the hot and cold States. The temperature interval of hot deformation is in the range of 350-480 °C. Important advantages of the grade is the extrusion of profiles and tubes with high speeds the expiry of 15-30 m/min above the acceptable during the pressing of alloys D1, AMg6 5-10 times.
Features of heat treatment Heat-treatable alloy. Alloy 1915 is zamotaylova, i.e. the strength characteristics depend little on the kind of quenching medium (water, air). As a result, the extruded profiles with a flange width of 10 mm may not be subject to hardening, because the cooling after extrusion in the air gives almost the same structure and the same properties as quenching in water after heating in the hardening furnaces. Alloy hardened during the aging process, as at room and at elevated temperatures.
Corrosion resistance The alloy has good resistance to corrosion, higher than the alloy D1.