Alloy ХН60КМЮВТБ (EK9)

Alloy KhN66VMTYUB (EI698MP; VZH136) Alloy KhN67VMTU (EP202; KhN67MVTU) Alloy KhN65KMVYUB (EP800) Alloy CrN65VMYUTL (EI893L) Alloy KhN65VMTU (EI893) Alloy CrN65VMMBU (EP914; VZH131) Alloy CrN65VBMYu (EP902) Alloy KhN62MVKYu (EI867) Alloy KhN62VMYUT (EP708) Alloy KhN62VMKU (EI867) Alloy KhN62BMKTU (EP742) Alloy CrN62BMVY (EP709) Alloy KhN60MYUVT (EP539) Alloy KhN60MVTU (EP487) Alloy KhN60M (EP367; 06Kh15N60M1) Alloy KhN60KMYUVTB (EC9) Alloy CrN60KMYUBVTF (EP962) Alloy KhN60KVYUMB (EP957) Alloy KhN59VG (EK82) Alloy KhN58MBYUD (EK61) Alloy KhN58MBYu (EK171; VZH159) Alloy KhN58VMKYR (EP238) Alloy KhN57MTVU (EP590) Alloy KhN73MBTU (EI698) Alloy EP539LMU Alloy ChS70 Alloy ChS104 Alloy CNK7 Alloy KhN80TBY (EI607; KhN80T1BY (EI607A)) Alloy KhN80 (EI334) Alloy KhN77TURU (EI437BU) Alloy KhN77TUR (EI437B) Alloy KhN75TBU (EI869) Alloy KhN75VMU (EI827) Alloy CrN75VMFU (EI827) Alloy KhN57MKYUVTBR (EP958) Alloy KhN71MTYUB (EI698P) Alloy KhN70MVU (EI828) Alloy KhN70MVTYUB (EI598) Alloy KhN70VMYUT (EI765) Alloy CrN70VMFTU (EI826) Alloy CrN70VMTUF (EI826; CrN70VMTUF) Alloy KhN70VMTU (EI617) Alloy KhN70 (EI442) Alloy KhN68VMTYUK (EP693) Alloy KhN67MBYu (EP782) Alloy VZHL12E Alloy ZhS6KP Alloy ZhS30 Alloy ZhS3 Alloy ZhS16 Alloy BC9L Alloy BC4LM Alloy BC4L Alloy VZHL2 Alloy VZhL18 Alloy VZHL16 Alloy VZHL14H (VZHL14) Alloy ZhS6U Alloy VZHL12U Alloy VZhL1 Alloy 67H26M (EI639; NIMO-25) Alloy 58NHVKTBU (EP877; ХН58VCBTU) Alloy 50H6MFA Alloy 50H3CU (EP967) Alloy 3MI3U Alloy 10X20H77TU Alloy 03Х20Н45М4БЧ (ChS42) Alloy 03X20H45M4BRZ (ChS43) Alloy KhN52KVMTYUB (EP975P) Alloy KhN56MBYUD (EK62) Alloy KhN56VMTU (EP199; VZh101) Alloy KhN56VMKU (EP109) Alloy KhN55MVU (EP454) Alloy KhN55MVTs (ChS57) Alloy KhN55MBYu (KhN63M9B2u; EP666) Alloy KhN55VMTFKU (EI929) Alloy KhN55VMTKU (EI929) Alloy KhN54KVMTYUB (EP962P) Alloy KhN53KVMTYUB (EP741P) Alloy KhN57VKYUTMBL (ZhS6) Alloy KhN51MTYUKFR (EP220) Alloy KhN51KVMTYUB (EP741NP) Alloy KhN50KVMTYUB (BB750) Alloy KhN50VMTYUB (EP648) Alloy KhN50VMTKFY (EP57) Alloy KhN45MVTYUBR (EP718) Alloy Kh15N60Yu3A (EP548) Alloy H95S3Yu (EP711) Alloy H95G (EP18) Alloy H70M (EP495)

Designation

Name The value
Designation GOST Cyrillic ХН60КМЮВТБ
Designation GOST Latin XH60KMJuBTB
Transliteration HN60KMYuVTB
The chemical elements CrNi60CoCuAlВTeBe
Name The value
Designation GOST Cyrillic ЭК9
Designation GOST Latin EK9
Transliteration EhK9
The chemical elements -

Description

Alloy ХН60КМЮВТБ used: for the production of pellet-prescisely obtained by hot pressing (extrusion), alloy smelted in open furnaces with subsequent vacuum arc remelting and intended for subsequent remelting and fabrication of castings and fasteners, and gas turbine aircraft industry.

Note

High-temperature Nickel-based alloy.
The recommended maximum operating temperature for a limited time — 800−900 °C.
The temperature of beginning of intensive scaling in air 1100−1150 °C.

Standards

Name Code Standards
Sectional and shaped rolling В32 TU 14-1-4426-88

Chemical composition

Standard C S P Mn Cr Si Ni Fe Al B Ti Mo Nb W Ce Co Sr Mg
TU 14-1-4426-88 0.1-0.15 ≤0.01 ≤0.015 ≤0.3 19-20 ≤0.3 The rest ≤1.5 3-4 ≤0.12 2-3 3-4 1.4-2 2.5-4 ≤0.02 4-6 ≤0.05 ≤0.05
Ni is the basis.
According to TU 14-1-4426-88, the chemical composition is given for the alloy grade KhN60KMYUVTB-VD (EC9-VD). Boron, strontium, magnesium are introduced into the metal by calculation and chemical analysis are not determined. In the finished metal, a chemical composition deviation according to the chromium content is allowed, plus 0.50%.

Mechanical characteristics

σB, MPa d y, %
Bars-pressestelle on the other 14-1-4426-88. Homogenizing annealing with 1160-1180 °C (aging for 3.0-3.5 h), air cooling
≥442 ≥8 ≥20

Description mechanical marks

Name Description
σB Limit short-term strength
d Elongation after rupture
y The relative narrowing

Technological properties

Name The value
Macrostructure and contamination The macrostructure of bars-prescisely on the other 14-1-4426-88 should not have cracks, bubbles, inclusions, visible to the naked eye.
Features of production Bars-pressestelle on the other 14-1-4426-88 come after etching. On the surface of pellet-prescisely allowed cracks, flaws, volosovichi that are not defects of the macrostructure.