Alloy MA2-1

Designation

Name The value
Designation GOST Cyrillic МА2-1
Designation GOST Latin MA2-1
Transliteration MA2-1
The chemical elements CuAl2-1

Description

Alloy MA2−1 is used: for the manufacture of semi-finished products (sheets, plates, rods, sheets, tubes, wire, stampings and forgings) by hot deformation; extruded sections with cross sectional area up to 12 cm2 and a diameter of the circumscribed circle of up to 150 mm; ingots and slabs intended for the production of panels, stampings complex configuration for welding constructions with maximum operating temperatures up to +150 °C — long, up to +200 °C — short-term.

Standards

Name Code Standards
Sectional and shaped rolling В52 GOST 13616-97, GOST 13617-97, GOST 13618-97, GOST 13619-97, GOST 13620-90, GOST 13621-90, GOST 13622-91, GOST 13623-90, GOST 13624-90, GOST 13737-90, GOST 13738-91, GOST 17575-90, GOST 17576-97, GOST 19657-84, GOST 29296-92, GOST 29303-92, GOST Р 50066-92, GOST Р 50067-92, GOST Р 50077-92
Non-ferrous metals, including rare metals, and their alloys В51 GOST 14957-76, OST 4.021.009-92, TU 1-4-015-80
Bars В55 GOST 18351-73
Pipes from non-ferrous metals and alloys В64 GOST 19441-74
Sheets and stripes В53 GOST 21990-76, GOST 22635-77, OST 4.021.048-92, TU 1-9-334-87, TU 1-9-365-78, TU 1-9-389-85

Chemical composition

Standard Mn Si Ni Fe Cu Al Zn Mg Be
GOST 14957-76 0.3-0.7 ≤0.1 ≤0.004 ≤0.04 ≤0.05 3.8-5 0.8-1.5 The rest ≤0.002
Mg is the basis.
According to GOST 14957-76 the mass fraction of other impurities is ≤ 0.30%. "Other impurities" include impurities whose permissible content limits are not indicated (≤), as well as impurities not included in the table, the content of which is not determined. Beryllium is not determined, but is introduced by calculation.

Mechanical characteristics

Section, mm sT|s0,2, MPa σB, MPa d y, % Brinell hardness number, MPa
Rolled steel in the delivery state
≥190 ≥240 ≥26 ≥18 -
Sheet metal in delivery condition of alloy MA2-1 and MA2-1pch 22635-77 according to GOST, OST 4.021.048-92 (samples transverse)
8-10.5 ≥145 ≥255 ≥8 - -
0.6-2.5 ≥155 ≥255 ≥10 - -
2.5-10.5 ≥145 ≥255 ≥8 - -
Plate hot rolled according to GOST 21990-76 without heat treatment in the state of delivery (longitudinal samples)
12-20 ≥137 ≥245 ≥7 - -
20-32 ≥137 ≥245 ≥6 - -
32-50 - ≥226 ≥6 - -
Extruded GOST 19657-84 without heat treatment in the state of delivery (in cross-section provided the cross-sectional area of the profile in cm2)
5-12 ≥145 ≥255 ≥8 - ≥42
5 ≥155 ≥265 ≥9 - ≥45
Bars and rods, hot-pressed in the delivery condition without heat treatment according to GOST 18351-73 (longitudinal samples)
160-200 - ≥245 ≥5 - -
8-160 ≥145 ≥255 ≥8 - -
Tubes extruded in the state of delivery according to GOST 19441-74 (samples)
- - ≥255 ≥9 - -

Description mechanical marks

Name Description
Section Section
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d Elongation after rupture
y The relative narrowing

Physical characteristics

Temperature Е, ГПа r, кг/м3 l, Вт/(м · °С) R, НОм · м
20 42 1790 963 120

A description of the physical symbols

Name Description
Е The normal elasticity modulus
r Density
l Coefficient of thermal conductivity
С Specific heat