Steel 17GS

03CrNiSteel 05G1B steel 06G2AF steel 06G2MFB steel 06G2FR steel 06CGSY steel Steel 07GBU Steel 07GFB (07GFB-U) 08G1NFB steel Steel 08G2MF (08G2MFA) 08G2S steel 08G2SFB steel Steel 08G2T (08G2T-U) 08G2FBT steel 08GBU steel Steel 08GBUTR Steel 09G2 Steel 09G2D Steel 09G2S (09G2SA) Steel 09G2SD Steel 09G2FB (09G2BT) 09GBU steel 09GNFB steel Steel 09GSNBTs 09CrNi2Ab steel 10G2B steel Steel 10G2BD 10G2BTU steel Steel 10G2S1 Steel 10G2S1D 10G2SB steel 10G2SFB steel 10G2T steel 10G2FB steel 10Г2ФБЮ steel 10GNB steel Steel 10GS2 10GT steel Steel 10ХГСН1Д (СХЛ-45) 10XDP steel Steel 10ХН1М (ВК-1А) 10KhNDM steel 10XNDP steel Steel 10ХСНД (СХЛ-4) Steel 12G (12GA) Steel 12G2AF Steel 12G2B Steel 12G2S Steel 12G2SB Steel 12G2SMF Steel 12G2SMFAU 12GN2MFAu steel 12NDU steel Steel 12GS (Sv-12GS) 12GSB steel 12GF steel 12ХГДАФ steel 12HSND steel Steel 13G1S (13G1S-U) Steel 13G1SB (13G1SB-U) 13G2AF steel 13GDF steel Steel 13GS (13GS-U) Steel 13GF (13GFA) Steel 14G2 Steel 14G2AF Steel 14G2AFD Steel 14GS Steel 14GF Steel 14ХГМДЦ Steel 14KhGS 15Г2АФД steel (15Г2АФДпс) 15G2SF steel 15G2SFD steel 15Г2ФБЮ steel 15GS steel 15GF steel 15GFD steel 15KhDP steel 15HSND steel Steel 16G (16GA) 16G2AF steel Steel 16G2AFD Steel 16G2SF (16G2SAF) 16GD steel 16GMYUCH steel 16GS steel 16GFB steel Steel 16D Steel 17G1S (17G1S-U) Steel 17GS Steel 18G2AF (18G2AFps) Steel 18Г2АФД (18Г2АФДпс) 18G2S steel 18YuT steel (Ch-33) Steel 19YuFT (Ch37) Steel 1Х2М1 Steel 20G2S 20GS steel Steel 20GS2 Steel 20GSF (20GSFL) Steel 20Х2Г2СР Steel 20KhG2Ts Steel 20ХГСС2 Steel 22G2 22GYu steel Steel 22C Steel 22Kh2G2AU Steel 22Kh2G2P Steel 23Cr2G2T Steel 25G2S Steel 25GS Steel 25C2P Steel 27GS Steel 28G2S1D Steel 28G2SFB (28G2SFBD) Steel 28C Steel 30HS2 Steel 32G2RPs Steel 35GS 45KhGMA steel Steel 80C Steel SVS-690 (Severstal-690) X56 steel

Designation

Name The value
Designation GOST Cyrillic 17ГС
Designation GOST Latin 17GC
Transliteration 17GS
The chemical elements 17MnС

Description

Steel 17GS used: for the manufacture of shells vehicles, bottoms, vessels, flanges and other welded parts working under pressure at temperatures from -40 °C to +475 °C; parts and elements of pipelines of steam and hot water nuclear power plants (NPP), with an estimated temperature not higher than 350 °C at an operating pressure of less than 2.2 MPa (22 kgf/cm2); welded longitudinal pipes of strength group K52 for construction of gas pipelines, oil pipelines and oil product pipelines; ekspandirovannogo longitudinal electric-welded pipes intended for construction of high pressure pipelines.

Note

Steel low-alloy silico-manganese. The degree of deoxidation — SP.
Steel 17GS provides strength grade sheet, universal broadband rental and roll-formed profiles KP 325 with plate thickness of 10 to 20 mm., KP 345 in thicknesses up to 10 mm. without the use of additional hardening treatment.

Standards

Name Code Standards
Classification, nomenclature and general norms В20 GOST 19281-89
Pipes steel and connecting parts to them В62 GOST 20295-85, GOST 24950-81, HUNDRED 79814898 105-2008, TU 14-3-1270-84, TU 14-159-170-87, TU 14-159-263-96, TU 14-158-153-05, TU 1303-002-08620133-01, TU 14-158-146-2004, TU 14-3-1573-96, TU 14-3-620-77
Sheets and stripes В23 GOST 82-70, GOST 5520-79, GOST 17066-94, GOST 19903-74, GOST 19904-90, GOST 103-2006, GOST 19282-73, GOST 19903-90, TU 14-1-4632-93
Sectional and shaped rolling В22 GOST 8278-83, GOST 8281-80, GOST 8282-83, GOST 8283-93, GOST 9234-74, GOST 11474-76
Sectional and shaped rolling В32 TU 14-1-1271-75, TU 14-136-367-2008
Sheets and stripes В33 TU 14-1-1921-76, TU 14-1-2584-79, TU 14-1-2917-80, TU 14-1-5241-93, TU 14-1-4431-88

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu N As Al V Ti Nb Ce
TU 14-1-1921-76 0.15-0.2 ≤0.025 ≤0.03 1-1.4 ≤0.3 0.4-0.6 ≤0.3 The rest ≤0.3 ≤0.012 ≤0.008 ≤0.05 - ≤0.03 - ≤0.03
GOST 19282-73 0.14-0.2 ≤0.04 ≤0.035 1-1.4 ≤0.3 0.4-0.6 ≤0.3 The rest ≤0.3 ≤0.008 ≤0.08 ≤0.05 - ≤0.03 - -
GOST 17066-94 0.14-0.2 ≤0.04 ≤0.035 1-1.4 ≤0.3 0.4-0.6 ≤0.3 The rest ≤0.3 ≤0.008 ≤0.08 ≤0.03 ≤0.1 ≤0.03 ≤0.03 -
TU 14-158-146-2004 ≤0.18 ≤0.015 ≤0.02 1-1.4 - 0.4-0.6 - The rest - ≤0.012 - - ≤0.08 - ≤0.07 -
TU 14-3-1573-96 0.15-0.2 ≤0.035 ≤0.035 1-1.4 ≤0.3 0.4-0.6 ≤0.3 The rest ≤0.3 ≤0.012 - - - - - -
Fe is the basis.
According to TU 14-1-1921-76, instead of Ce, Ca≤0.020% can be introduced.
According to GOST 17066-94, the mass fraction of arsenic is allowed up to 0.015%, with the mass fraction of phosphorus being not more than 0.030%.
According to GOST 19282-73, it is allowed to modify steel with calcium and rare-earth elements from the calculation of the introduction of not more than 0.02% calcium and 0.05% rare-earth elements into the metal.
According to GOST 19281-89 and GOST 19282-73, it is allowed to add aluminum and titanium from the calculation of the mass fraction in the rolled aluminum - no more than 0.050%, titanium - no more than 0.030%.
According to GOST 5520-79, the mass fraction of arsenic can be up to 0.15% in the smelting of steel from the Kerch ore, while the mass fraction of phosphorus should not be more than 0.030%. At the request of the consumer, the mass fraction of sulfur should not exceed 0.025, 0.030 or 0.035%, and phosphorus 0.030 or 0.035%. When steel is smelted in electric furnaces, the mass fraction of nitrogen must be ≤ 0.012%.
According to TU 14-3-1573-96 carbon equivalent of Se ≤ 0.46%.
According to TU 14-158-146-2004 the chemical composition is shown for the ladle sample for the 1st level of quality of pipes made of steel of the grades 17GS, 17GS PL-1, 17GS PL-2. Niobium and vanadium are optional and are introduced into the steel by calculation with the manufacturer's agreement with the consumer.

Mechanical characteristics

Section, mm sT|s0,2, MPa σB, MPa d5, % d4 kJ/m2, кДж/м2
Steel hot-rolled sheet in the delivery condition
2-3.9 - ≥510 ≥19 - -
5-9 ≥350 ≥520 ≥23 - -
Longitudinal electric-welded pipes TU 1303-002-08620133-01 in the delivery condition (in cross-section shows the thickness of the wall)
10-20 ≥335 490-640 ≥23 - ≥340
6-10 ≥345 510-660 ≥23 - ≥440
Rolled steel in the delivery state
≤41 - ≥520 ≥23 - -
Rolled plates as supplied by TU 14-1-5241-93. Quenching + Tempering (samples transverse)
10-50 ≥325 ≥450 ≥21 - -
8-10 ≥345 ≥490 ≥23 - -
Sheet 2-6, 10-12, 16, 18-22 categories, heat-treated, in the state of delivery GOST 5520-79
≤10 ≥345 ≥510 ≥23 - -
The plates and universal broadband in the state of delivery GOST 19282-73
≤10 ≥345 ≥510 ≥23 - -
Sheet 2-6, 10-12, 16, 18-22 categories, heat-treated, in the state of delivery GOST 5520-79
10-20 ≥335 ≥490 ≥23 - -
The plates and universal broadband in the state of delivery GOST 19282-73
10-20 ≥335 ≥490 ≥23 - -
Sheet metal in delivery condition on the other 14-1-4632-93 (samples transverse)
10-25 335-530 490-690 ≥23 - -
5-10 345-540 490-690 ≥23 - -
Hot rolled plates for gas pipes. In the delivery condition. Group strength K52
7-10 ≥355 ≥510 ≥24 - ≥590
Sheets of thermo 2-6, 10-12, 16 and 18 categories in sostayanii delivery (transverse sample)
4-20 ≥320 490-610 ≥22 - ≥480
Pre-painted steel sheet of high-strength steel in the delivery state GOST 17066-94
0.5-3.9 ≥355 ≥510 - ≥18 -
0.5-3.9 ≥355 ≥480 - ≥18 -
Longitudinal electric-welded pipes of oil and gas as delivered at TU 14-3-1573-96 (samples transverse; column cross section - outer diameter; in the graph the value is KCU KCU-40 °C)
530, 630, 720, 820, 1020 ≥350 ≥510 ≥20 - ≥294

Description mechanical marks

Name Description
Section Section
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture
d4 Elongation after rupture
kJ/m2 Toughness

Technological properties

Name The value
Weldability Welded without any restrictions.