Equivalent

Grade analogue W. Nr. Aisi Uns En Order
ВТ22 Buy from stock, view availability

Technical characteristics

Titanium grade gost VT22 alloy relates to a transition type. It possesses high strength-to-density ratio of more than 960 MPa. It was invented in 1965 by VIAM. Later, there were offered modifications of this alloy.

Percentage composition according to GOST 19807−91

Fe C Si Cr Mo V N Ti Al Zr O H Residual elements
0.5 — 1.5 ≤0.1 ≤0,15 0.5 — 1.5 4 — 5.5 4 — 5.5 ≤0.05 79.4 — 86.3 4.4 — 5.7 ≤ 0.3 ≤0,18 ≤0.015 ≤ 0.3

Bar section of titanium gost VT22 undergoes thermohardening at 750° +480° C for 16 hours.

Semi-fabricate Heat treatment Thickness, mm Strength (MPa) KCU J/cm³ Plasticity δ%
Bar Annealing up to 200 mm 1080 — 1230 more than 25 more than 7%
— «--- Annealing 25 — 60 1070 — 1226 more than 30 more than 10%
— «--- Condition of supply 65 — 100 1100 — 1300 more than 30 more than 8%
— «--- Condition of supply 101 — 130 1100 — 1300 more than 30 more than 8%
Bar Condition of supply 140 — 250 1100 — 1300 more than 30 more than 8%
— «--- Thermohardening 870 °C + 500 °C 16 h. up to 20 mm 1375 — 1520 30 — 60 7 — 10%
— «--- Thermohardening + age-hardening more than 40 mm 1200 — 1300 --- more than 6%
— «--- Annealing 700° up to 300° up to 100 mm 1080 — 1225 30 — 60 8 — 16%
— «---

Annealing 750° 0,5 h.

up to 350°, V

Ø20 mm 1147 34 16%
Bar

Annealing 750° 1 h.

up to 350°, V

Ø30 mm 1073 — 1092 37 — 44 18 — 20%
— «--- Annealing Ø50 mm 1140 39 16%
— «--- Thermohardening 780 °C + 400 °C 16 h. 14 mm 1860 --- 3.5%
— «--- Thermohardening + age-hardening   1680 --- 10%
Bar Thermohardening 750 °C + age-hardening, 500 °C 10 hours   1323 — 1421 --- 7 — 11
— «--- Thermohardening 700−750° + age-hardening, 450−500°  

More than

1274 — 1470

--- 8 — 10%
Forged bars

Annealing 780° 1 h.

up to 400°, V

14x14 1127 --- 16.7%
Bar 840° 1 h. up to 750°, 3 h, V +620° 4 h, V 60 — 100 1108 — 1133 28 — 42 12.4 — 16%
— «--- Thermohardening + age-hardening 1370 — 1520 5% ---  
— «--- Annealing 1080 — 1230 more than 10% more than 30  
— «--- Thermohardening 880° 1058 — 1100 10 — 13    
Bar Isothermal annealing 1250 13% ---  
— «--- Thermohardening 700 — 750° + age-hardening 450 — 500°С more than 1300   ---  
— «--- 1490 11% 17.4    

There can be such types of cutting: short transverse, longitudinal, high-altitude, tangential section.

Heat resistance is characterized by the highest stress — creep limit. Under its influence, a material is deformed by a given amount at a given temperature.

Heat resistance of titanium bar gost VT22

Range of sizes Heat treatment Creep limit 0,2/100 t°C
Bar Annealing 764 300°
— «--- Annealing 402 350°
— «--- Thermohardening + age-hardening 890 250°
— «--- Thermohardening + age-hardening 880 300°

Long-term strength is a maximum stress that can disrupt a material after a certain time at a given temperature. The more load duration and the higher temperature are, the less a resistance to rupture is.

Long-term strength titanium bar of gost VT22

Thickness Heat treatment t°С Long-term strength (MPa)  
25 mm Annealing 300° 880  
25 mm — «--- 350° 800  
25 mm — «--- 400° 650  
80 mm Age-hardening and thermohardening 250° 980  
80 mm Age-hardening and thermohardening 300° 950  
80 mm Age-hardening and thermohardening 350° 850  
Bar of gost VT22 Heat treatment Long-term strength (MPa) t°С  
25 mm Annealing 880 300°  
25 mm 350° 800    
25 mm 400° 650    
80 mm Age-hardening and thermohardening 980 250°  
80 mm 300° 950    
80 mm 350° 850    

Fatigue resistance of bar gost VT22

Bar Thickness, mm Heat treating R Load configuration Endurance strength 10.000.000
Gost VT22 25 Annealing — 1 Symmetrical loading More than 519 MPa
— «--- 100 — «--- — 1 Bending through an angle in one platitude 505 MPa
— «--- 20 — «--- — 1 Bending through an angle in one platitude 580 MPa

Testing data of repeated static load (low-cycle fatigue)

Grade gost VT22 Thickness Heat treatment / structure Strength (MPa) N х 1000
Bar 80 mm Annealing 8 1200
— «--- 80 mm Fine-grained 11 1225
— «--- 80 mm Polygonized 9.5 1225

Application

Semi-fabricates of gost VT22 alloy are indispensable in manufacture of attaching fittings, large strength part of air-frame, wings, landing gears, parts of all-cargo aircraft control system, parts for gas-turbine engine.

Supplier

«Auremo» titanium gost VT22 wire, bar supplier offers to buy titanium products by wholesale. There is a wide range of half-finished goods in stock. They comply with GOST and International quality Standards. Wire, rod, bar of titanium gost VT22 are always in stock. You can buy goods for the best price from a supplier. Buy titanium gost VT22 wire, bar in a moment! Titanium gost VT22 wire, bar price is privileged for wholesale customers.

Buy at a bargain price

«Auremo» supplier is a recognized expert on a market of titanium mill-products. We have offices in Eastern Europe, so we are able to make a prompt cooperation with business partners. Experience of our company allows you to easily buy titanium gost VT22 wire, bar in a large variety by wholesale. A quality complies with GOST (all-Union State Standards) and International Standards. «Auremo» company is a reliable titanium gost VT22 wire, bar supplier of titanium mill-products that invites all the wishing to a partnership. We have the best price-quality ratio. Titanium gost VT22 wire, bar price is privileged for wholesale customers. All products are certificated. A delivery service will supply your order in the shortest possible time. Titanium gost VT22 wire, rod, bar are always in stock. There is the best price in this segment of mill-products.